Effect of Heating Rate and Temperature on the Carbonization Process of Commercial Viscose fibers
Main Article Content
Abstract
Effect of heating rate and temperature on the carbonization process of commercial Viscose (cellulosic based precursor) fibers are investigated in the present study. Several carbonization experiments are conducted on stabilized fibers with carbon content of 59.72 wt% and diameter of about 13.3 μm. The Viscose fibers are stabilized with the catalyst of mixture urea/diammonium hydrogen phosphate in air at temperature of 250 °C. The stabilized fibers are then carbonized in argon at temperature ranging from 600 °C to 1200 °C with the heating rate of 5 °C·min⁻¹. Experimental results show that the obtained fibers have carbon content above 94 wt% and diameters of about 8μm. These fibers are potential to produce activated carbon fibers.
Keywords
Carbonization, carbon fibers, Viscose, cellulose based precursor
Article Details
References
[1] Peter Morgan, “Carbon Fibers and their Composite – Chapter 4: Precursor of Carbon Fiber Manufacture”, Taylor & Francis Group, 2005.
[2] D. D. Edie & R. J. Defendorf, “Carbon Fiber Manufacturing”, Carbon-Carbon Materials and Composite, Edited by John D. Buckley & Dan D. Edie, Noyes Publications, 1993.
[3] Nguyễn Hữu Sơn, Phạm Văn Cường, Vũ Lê Hoàng, Lê Thái Hưng, “Ổn định hóa sợi Viscose thương mại cho chế tạo sợi các bon”, Hội nghị Luyện kim và Khoa học vật liệu tiên tiến – Sự phát triển bền vững của nền công nghiệp, ĐH Bách Khoa Hà Nội, 10/2016, pp. 34–39.
[4] Nguyễn Hữu Sơn, Phạm Văn Cường, Vũ Lê Hoàng, Lê Thái Hưng, “Ảnh hưởng của hàm lượng chất xúc tác đến quá trình ổn định hóa sợi Viscose thương mại cho chế tạo sợi các bon”, Tạp chí Khoa học Công nghệ Kim loại, số 76, (2018), pp. 38–43.
[5] Peter Morgan, “Carbon Fibers and their Composite – Chapter 6: Carbon Fiber Production using Cellulosic based Precursor”, Taylor & Francis Group, 2005.
[6] Bacon, R. and M. Tang, “Carbonization of Cellulose Fibers-I: Low Temperature Pyrolysis”, Pergamon Press Ltd, Carbon, vol 2, (1964) pp. 211–220.
[2] D. D. Edie & R. J. Defendorf, “Carbon Fiber Manufacturing”, Carbon-Carbon Materials and Composite, Edited by John D. Buckley & Dan D. Edie, Noyes Publications, 1993.
[3] Nguyễn Hữu Sơn, Phạm Văn Cường, Vũ Lê Hoàng, Lê Thái Hưng, “Ổn định hóa sợi Viscose thương mại cho chế tạo sợi các bon”, Hội nghị Luyện kim và Khoa học vật liệu tiên tiến – Sự phát triển bền vững của nền công nghiệp, ĐH Bách Khoa Hà Nội, 10/2016, pp. 34–39.
[4] Nguyễn Hữu Sơn, Phạm Văn Cường, Vũ Lê Hoàng, Lê Thái Hưng, “Ảnh hưởng của hàm lượng chất xúc tác đến quá trình ổn định hóa sợi Viscose thương mại cho chế tạo sợi các bon”, Tạp chí Khoa học Công nghệ Kim loại, số 76, (2018), pp. 38–43.
[5] Peter Morgan, “Carbon Fibers and their Composite – Chapter 6: Carbon Fiber Production using Cellulosic based Precursor”, Taylor & Francis Group, 2005.
[6] Bacon, R. and M. Tang, “Carbonization of Cellulose Fibers-I: Low Temperature Pyrolysis”, Pergamon Press Ltd, Carbon, vol 2, (1964) pp. 211–220.